PTFE热收缩套管由聚四氟乙烯(PTFE)材料制成,具有耐高温(260℃)、耐腐蚀、高绝缘、机械强度佳等特性。其广泛用于电子、计算机、电热、航天、军事、通讯等重要科技工业,如微型变压器等。通常用在液压管道及其管道结合部位以保护管道不受腐蚀。由于它具有非常高的机械强度和极低的摩擦系数,所以是保护受力轴和轴相关产品的理想产品。
特性
v 收缩比:1.7:1
v 优异的的阻燃性
v 耐高温260℃
v 杰出的机械性能和耐化学腐蚀性能
v 符合ROHS、REACH等环保规范
v 颜色
v 标准颜色:透明
操作温度范围
v 连续使用温度:-67℃~260℃
v **完全收缩温度:350℃
符合标准
v SAE AMS-DTL-23053/12
性能指标
性能 |
指标要求 |
测试方法 |
典型值 |
纵向收缩率 |
≤10% |
ASTM D 2671 |
≤5% |
抗张强度 |
17.3MPa min |
ASTM D 638 |
≥22MPa |
断裂伸长率 |
200% min |
ASTM D 638 |
≥300% |
绝缘耐压和击穿 |
2500V,60sec,不击穿 |
ASTM D 2671 |
通过 |
体积电阻率 |
1015Ω•cm min |
ASTM D 876 |
≥1016Ω•cm |
腐蚀性 |
无腐蚀 |
ASTM D 2671 |
无腐蚀 |
阻燃性 |
VW-1 |
UL224 |
通过 |
介电常数 |
2.1 |
||
摩擦系数 |
0.1 |
规格尺寸
规格 |
收缩前(mm) |
完全收缩后(mm) |
标准包装 (m/条或m/卷) |
||
AWG |
公制 |
内径(min) |
内径(max) |
壁厚 |
|
30 |
Ф0.8 |
0.8 |
0.4 |
0.23+0.05 |
1.22/200 |
28 |
Ф0.9 |
0.9 |
0.5 |
0.23+0.05 |
1.22/200 |
26 |
Ф1.1 |
1.1 |
0.6 |
0.25+0.05 |
1.22/200 |
34 |
Ф1.2 |
0.2 |
0.7 |
0.25+0.05 |
1.22/200 |
22 |
Ф1.4 |
1.4 |
0.8 |
0.30+0.08 |
1.22/200 |
20 |
Ф1.5 |
1.5 |
1.0 |
0.30+0.08 |
1.22/200 |
18 |
Ф1.9 |
1.9 |
1.25 |
0.30+0.08 |
1.22/200 |
16 |
Ф2.3 |
2.3 |
1.6 |
0.30+0.08 |
1.22/100 |
14 |
Ф3.0 |
3.0 |
1.85 |
0.30+0.08 |
1.22/100 |
12 |
Ф3.8 |
3.8 |
2.3 |
0.30+0.08 |
1.22/100 |
10 |
Ф4.8 |
4.8 |
2.85 |
0.30+0.08 |
1.22/100 |
8 |
Ф6.1 |
6.1 |
3.6 |
0.38+0.08 |
1.22/100 |
6 |
Ф7.6 |
7.6 |
4.5 |
0.38+0.08 |
1.22/100 |
4 |
Ф9.4 |
9.4 |
5.7 |
0.38+0.08 |
1.22/50 |
2 |
Ф10.9 |
10.9 |
7.1 |
0.38+0.08 |
1.22/50 |
0 |
Ф11.9 |
11.9 |
8.8 |
0.38+0.08 |
1.22/50 |
其他规格尺寸可定制
PTFE 260℃ High-temperature PTFE Heat Shrinkable Tubing
Application
PTFE heat shrinkable tubing is made of PTFE with excellent high-temperature performance, chemical resistance, high insulation and excellent mechanical properties. Designed to provide insulation and mechanical protection in severe chemical and thermal environments. Widely used in electronic, aerospace, military and communication fields. Used to cover hydraulic hose and couplings to prevent contamination and corrosion. The high mechanical strength and extremely low coefficient of friction make it good for reducing damage to bearing shafts and similar applicationns.
Characteristics
v Shrink ratio: 1.7:1
v Excellent flammability
v High temperature resistant to 260℃
v Superior physical and chemical properties.
v ROHS and REACH compliant.
Color
v Standard color: Clear
Operating Temperature Range
v Operating temperature: -67℃~260℃
v Minimum fully recovery temperature: 350℃
Approvals
v SAE AMS-DTL-23053/12
Property
Property |
Requirement |
Test method |
Typical data |
Longitudinal shrinkage |
≤10% |
ASTM D 2671 |
≤5% |
Tensile strength |
17.3MPa min |
ASTM D 638 |
≥22MPa |
Elongation at break |
200% min |
ASTM D 638 |
≥300% |
Dielectric voltage withstand |
2500V,60sec,no breakdown |
ASTM D 2671 |
Pass |
Volume resistivity |
1015Ω•cm min |
ASTM D 876 |
≥1016Ω•cm |
Copper corrosion |
No corrosion |
ASTM D 2671 |
No corrosion |
Flammability |
VW-1 |
UL224 |
Pass |
Dielectric constant |
2.1 |
||
Friction coefficient |
0.1 |
Sizes
Size |
As supplied (mm) |
After recovered(mm) |
Standard packing (m/pc,m/roll) |
||
AWG |
mm |
Inside diameter(min) |
Inside diameter max |
Wall thickness |
|
30 |
Ф0.8 |
0.8 |
0.4 |
0.23+0.05 |
1.22/200 |
28 |
Ф0.9 |
0.9 |
0.5 |
0.23+0.05 |
1.22/200 |
26 |
Ф1.1 |
1.1 |
0.6 |
0.25+0.05 |
1.22/200 |
34 |
Ф1.2 |
0.2 |
0.7 |
0.25+0.05 |
1.22/200 |
22 |
Ф1.4 |
1.4 |
0.8 |
0.30+0.08 |
1.22/200 |
20 |
Ф1.5 |
1.5 |
1.0 |
0.30+0.08 |
1.22/200 |
18 |
Ф1.9 |
1.9 |
1.25 |
0.30+0.08 |
1.22/200 |
16 |
Ф2.3 |
2.3 |
1.6 |
0.30+0.08 |
1.22/100 |
14 |
Ф3.0 |
3.0 |
1.85 |
0.30+0.08 |
1.22/100 |
12 |
Ф3.8 |
3.8 |
2.3 |
0.30+0.08 |
1.22/100 |
10 |
Ф4.8 |
4.8 |
2.85 |
0.30+0.08 |
1.22/100 |
8 |
Ф6.1 |
6.1 |
3.6 |
0.38+0.08 |
1.22/100 |
6 |
Ф7.6 |
7.6 |
4.5 |
0.38+0.08 |
1.22/100 |
4 |
Ф9.4 |
9.4 |
5.7 |
0.38+0.08 |
1.22/50 |
2 |
Ф10.9 |
10.9 |
7.1 |
0.38+0.08 |
1.22/50 |
0 |
Ф11.9 |
11.9 |
8.8 |
0.38+0.08 |
1.22/50 |
Other sizes are available upon request.